Tabular Alumina Sand/powder Use For Refractory Material

Tabular Alumina Sand/powder Use For Refractory Material,has good heat resistance and good volumetric temperature shock ability. Crystal shape plate to increase the mechanical strength of the particles; internal structure full of closed pores, high bulk density, low apparent porosity and water absorption to reduce the amount of reused fluids; With good physical properties such as: high refractory, excellent thermal shock resistance, low shrinkage and good strength under thermal load, etc.

$799.00 $699.00 /MT

Tabular Alumina Sand/powder Use For Refractory Material

Description:

Tabular alumina sand/powder has good heat resistance and good volumetric temperature shock ability. Crystal shape plate to increase the mechanical strength of the particles; internal structure full of closed pores, high bulk density, low apparent porosity and water absorption to reduce the amount of reused fluids; With good physical properties such as: high refractory, excellent thermal shock resistance, low shrinkage and good strength under thermal load, etc. Meanwhile, high cleanliness preventing damage to machines. Haixu abrasives is your best choice as refractory material/ceramic material and insulation materials.

Chemical analysis:

StyleChemical IndexPhysical Index
Al2O3%SiO2%Fe2O3%Na2O%Volume density
(g/cm3)
waterabsorptionapparent porosity
0-1mm
0-0.5mm
1-3mm
3-5mm
3-6mm
5-8mm
99.2min0.1max0.1max0.4max3.5  1.5 5max
200#-0
320#-0
325#
99.1min0.1max0.1max0.4max   3.5  1.5 5max
Tabular Alumina Sand/powder Use For Refractory Material

Tabular alumina sand/powder application:

It is an ideal refractory material, either can be used in various refractory alumina, or can be add in other unshaped refractories.

Our warehouse:

Tabular Alumina Sand/powder Use For Refractory Material

Package for tabular alumina:

1000kgs/jumbo bag

25kgs/pvc bag, 40 pvc bags/jumbo ba

Weight1000 kg
Dimensions90 × 90 × 90 cm
PDF-LOGO-100-.png

TDS not uploaded

PDF-LOGO-100-.png

MSDS not uploaded

Please enter correct URL of your document.

Scroll to Top